UV monomer various viscosity approximate conversion table
centipoise.
UV monomer centipoise (cP) is the Z-small unit of dynamic viscosity, dynamic viscosity indicates that the liquid flows under a certain shear stress when the measure of internal friction, the value of the shear stress added to the flowing liquid and the ratio of the shear rate, in the international system of units to Pa-s, the customary use of cP said.
Format tube.
Format tube viscometer is an inner diameter of about 10.75mm, 115mm high with a stopper glass tube, the above in 100 and 108mm have two scale lines. Generally 20 pieces in a box. It is used to hold liquid specimens and is widely used in coating research laboratories and in the construction of spring and paint manufacturing industries.
Measurement of the time loaded with liquid to 100mm scale, thermostat after plugging the plug to 108mm inscribed line, continue to thermostat for 10min, quickly inverted viscosity tube, and viscosity tube placed vertically in the 25 ℃ water bath, to determine the bubble rise to the top of the viscosity tube time required. The result is expressed in seconds, and 25℃ is indicated.
Stormer viscometer.
Stormer viscometer is mainly used to determine paint and other test instruments that use KU value to express the viscosity of paint, the instrument does not use weights and can read the KU value of the tested sample directly from the display, application range: paints, coatings, inks, adhesives, pastes.
Rotary viscometer.
Rotary viscometer is used to measure the viscous resistance of liquids and liquid dynamic viscosity, widely used to determine the viscosity of various fluids such as grease, paint, plastic, food, medicine, cosmetics, adhesive products, paper chemicals, etc. It is a precision instrument for monitoring and controlling the stability of product quality in production.
Engler Viscometer.
Engler viscometer is designed and manufactured in accordance with the national standard GB/T 266 “petroleum products Engler viscosity determination method” and the national industry standard JTJ 052 “highway engineering asphalt and asphalt mixture test procedures” in T0622 “asphalt Engler viscosity test (Engler viscometer method)” requirements, suitable for the determination of liquid in a certain temperature, volume of the conditions, from the Engler viscometer outflow Time (seconds) and distilled water at 20 ℃ out of the time (seconds) ratio, that is, the liquid’s Engler viscosity, the unit for Engler degrees. This instrument can test 2 specimens at the same time in the same temperature environment and generate the average value of time, which is the ideal instrument for determining the Englishtick viscosity value of petroleum products and asphalt products.
Ford 4# cup.
Ford (Ford) cup according to the American Society for Testing and Materials paint and raw materials standards ASTM D 1200, D333, D365 in the production, used to determine the viscosity of ink, paint, paint and other viscosity more convenient viscometer. It is refined from a high-quality aluminum cup with a small hole at the bottom and a capacity of about 100ml. Ford (Ford) cup by measuring the aluminum cup in a certain capacity of the test material from the bottom of the small hole out of the time required to measure the viscosity of the test material.
DIN viscosity cups.
UV monomer DIN viscosity cups are very simple to use, made of anodized aluminum with stainless steel orifices, and measure the consistency of paints, varnishes and similar products. The measured kinetic viscosity is usually expressed in terms of the number of seconds it takes to flow out. There are DIN 2#, 3# and 4# cups.
Coated-4 cups.
UV monomer coated-4 cup, is a kind of viscosity cup widely used in China. Designed according to GB/T 1723-93, it is suitable for measuring the conditional viscosity of coatings and other related products (outflow time is not more than 150 seconds). Under certain temperature conditions, measure the quantitative specimen from the specified diameter of the hole all outflow time, expressed in S.
| 聚硫醇/聚硫醇 | ||
| DMES 单体 | 双（2-巯基乙基）硫醚 | 3570-55-6 |
| DMPT 单体 | THIOCURE DMPT | 131538-00-6 |
| PETMP 单体 | 季戊四醇四(3-巯基丙酸酯) | 7575-23-7 |
| PM839 单体 | 聚氧（甲基-1,2-乙二基） | 72244-98-5 |
| 单官能团单体 | ||
| HEMA 单体 | 甲基丙烯酸 2-羟乙基酯 | 868-77-9 |
| HPMA 单体 | 甲基丙烯酸羟丙酯 | 27813-02-1 |
| THFA 单体 | 丙烯酸四氢糠酯 | 2399-48-6 |
| HDCPA 单体 | 氢化双环戊烯丙烯酸酯 | 79637-74-4 |
| DCPMA 单体 | 甲基丙烯酸二氢双环戊二烯酯 | 30798-39-1 |
| DCPA 单体 | 丙烯酸二氢双环戊二烯酯 | 12542-30-2 |
| 二氯丙烯酰亚胺单体 | 甲基丙烯酸二环戊氧基乙酯 | 68586-19-6 |
| DCPEOA 单体 | 丙烯酸二环戊烯基氧基乙基酯 | 65983-31-5 |
| NP-4EA 单体 | (4) 乙氧基化壬基酚 | 50974-47-5 |
| LA 单体 | 丙烯酸十二烷基酯/丙烯酸十二烷基酯 | 2156-97-0 |
| THFMA 单体 | 甲基丙烯酸四氢糠酯 | 2455-24-5 |
| PHEA 单体 | 2-苯氧基乙基丙烯酸酯 | 48145-04-6 |
| LMA 单体 | 甲基丙烯酸月桂酯 | 142-90-5 |
| IDA 单体 | 丙烯酸异癸酯 | 1330-61-6 |
| IBOMA 单体 | 甲基丙烯酸异冰片酯 | 7534-94-3 |
| IBOA 单体 | 丙烯酸异冰片酯 | 5888-33-5 |
| EOEOEA 单体 | 2-(2-乙氧基乙氧基)丙烯酸乙酯 | 7328-17-8 |
| 多功能单体 | ||
| DPHA 单体 | 双季戊四醇六丙烯酸酯 | 29570-58-9 |
| DI-TMPTA 单体 | 二（三羟甲基丙烷）四丙烯酸酯 | 94108-97-1 |
| 丙烯酰胺单体 | ||
| ACMO 单体 | 4-丙烯酰基吗啉 | 5117-12-4 |
| 双功能单体 | ||
| PEGDMA 单体 | 聚乙二醇二甲基丙烯酸酯 | 25852-47-5 |
| TPGDA 单体 | 三丙二醇二丙烯酸酯 | 42978-66-5 |
| TEGDMA 单体 | 三乙二醇二甲基丙烯酸酯 | 109-16-0 |
| PO2-NPGDA 单体 | 丙氧基新戊二醇二丙烯酸酯 | 84170-74-1 |
| PEGDA 单体 | 聚乙二醇二丙烯酸酯 | 26570-48-9 |
| PDDA 单体 | 邻苯二甲酸二乙二醇二丙烯酸酯 | |
| NPGDA 单体 | 新戊二醇二丙烯酸酯 | 2223-82-7 |
| HDDA 单体 | 二丙烯酸六亚甲基酯 | 13048-33-4 |
| EO4-BPADA 单体 | 乙氧基化 (4) 双酚 A 二丙烯酸酯 | 64401-02-1 |
| EO10-BPADA 单体 | 乙氧基化 (10) 双酚 A 二丙烯酸酯 | 64401-02-1 |
| EGDMA 单体 | 乙二醇二甲基丙烯酸酯 | 97-90-5 |
| DPGDA 单体 | 二丙二醇二烯酸酯 | 57472-68-1 |
| 双-GMA 单体 | 双酚 A 甲基丙烯酸缩水甘油酯 | 1565-94-2 |
| 三官能单体 | ||
| TMPTMA 单体 | 三羟甲基丙烷三甲基丙烯酸酯 | 3290-92-4 |
| TMPTA 单体 | 三羟甲基丙烷三丙烯酸酯 | 15625-89-5 |
| PETA 单体 | 季戊四醇三丙烯酸酯 | 3524-68-3 |
| GPTA ( G3POTA ) 单体 | 丙氧基三丙烯酸甘油酯 | 52408-84-1 |
| EO3-TMPTA 单体 | 三羟甲基丙烷三丙烯酸乙氧基化物 | 28961-43-5 |
| 光阻单体 | ||
| IPAMA 单体 | 2-异丙基-2-金刚烷基甲基丙烯酸酯 | 297156-50-4 |
| ECPMA 单体 | 1-乙基环戊基甲基丙烯酸酯 | 266308-58-1 |
| ADAMA 单体 | 1-金刚烷基甲基丙烯酸酯 | 16887-36-8 |
| 甲基丙烯酸酯单体 | ||
| TBAEMA 单体 | 2-(叔丁基氨基)乙基甲基丙烯酸酯 | 3775-90-4 |
| NBMA 单体 | 甲基丙烯酸正丁酯 | 97-88-1 |
| MEMA 单体 | 甲基丙烯酸 2-甲氧基乙酯 | 6976-93-8 |
| i-BMA 单体 | 甲基丙烯酸异丁酯 | 97-86-9 |
| EHMA 单体 | 甲基丙烯酸 2-乙基己酯 | 688-84-6 |
| EGDMP 单体 | 乙二醇双(3-巯基丙酸酯) | 22504-50-3 |
| EEMA 单体 | 2-甲基丙-2-烯酸 2-乙氧基乙酯 | 2370-63-0 |
| DMAEMA 单体 | 甲基丙烯酸 N,M-二甲基氨基乙酯 | 2867-47-2 |
| DEAM 单体 | 甲基丙烯酸二乙氨基乙酯 | 105-16-8 |
| CHMA 单体 | 甲基丙烯酸环己基酯 | 101-43-9 |
| BZMA 单体 | 甲基丙烯酸苄酯 | 2495-37-6 |
| BDDMP 单体 | 1,4-丁二醇二（3-巯基丙酸酯） | 92140-97-1 |
| BDDMA 单体 | 1,4-丁二醇二甲基丙烯酸酯 | 2082-81-7 |
| AMA 单体 | 甲基丙烯酸烯丙酯 | 96-05-9 |
| AAEM 单体 | 甲基丙烯酸乙酰乙酰氧基乙基酯 | 21282-97-3 |
| 丙烯酸酯单体 | ||
| IBA 单体 | 丙烯酸异丁酯 | 106-63-8 |
| EMA 单体 | 甲基丙烯酸乙酯 | 97-63-2 |
| DMAEA 单体 | 丙烯酸二甲胺基乙酯 | 2439-35-2 |
| DEAEA 单体 | 2-(二乙基氨基)乙基丙-2-烯酸酯 | 2426-54-2 |
| CHA 单体 | 丙-2-烯酸环己基酯 | 3066-71-5 |
| BZA 单体 | 丙-2-烯酸苄酯 | 2495-35-4 |
立即联系我们！