Description
LA-D5433 / Polyether modified polydimethyl siloxane
| Composition | Polyether modified polydimethyl siloxane |
| Appearance | slight yellowish clear liquid(paste at low temperature) |
| Solvent | —— |
| Density | 1.01-1.05g/ml(25±1)℃ |
| Viscosity | 25-60s(Tu-4 viscometer)(25±0.2)℃ |
| Active substance | 100% |
| Flash point | ＞100℃ |
Note: This datasheet is intended to give typical results, not standard.Subject to COA.
Application system
Water-based, Solvent-based, UV Cure
Properties
● Excellent compatibility in varnish.
● Provide a stronger reduction of the surface tension.
● Reduce the friction coefficient. Increase slip and improve scratch resistance.
● Good recoating and minimal influence on adhesion of coating films at suitable addition and baking temperature.
● Excellent property of anti-crater.
● Good water-solubility.
● Hazy and viscous may occure at low temperatures. It would become clear and flow after heated. This will not influence the quality
Incorporation
Easy to add with pre-diluted solvent the same as that in the coating system. Can added as post-addition.
Suggest addition
Addition to total formulation 0.05-0.5%
Storage stability
Keep intact 24 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediatelyafter use.
Applicate recommendation
| Transparency in varnish | 5 |
| Defoaming | 0 |
| Dynamic surface tension | 5 |
| Static surface tension | 5 |
| Slip | 4 |
| Prevent orange peel | 1 |
0=unavailable 5=very effective
package
25KG / 180KG
Storage:
Being kept in dry, clean warehouse with well ventilation.
Avoid exposing to light and heating.
Protecting the product from leakage, rain and insolation during transportation.